| 不锈钢纤维酸性电解处理 |
| 添加时间：2020/8/17 17:05:10 浏览次数： |
| 不锈钢纤维酸性电解处理，铜包集束不锈钢纤维细拉丝后酸解处理，电解后不锈钢纤维纯水清洗烤干；作为其酸性电解溶解液添加物，提高不锈钢纤维集束拉丝后酸性电解分离速度，促进铜的快速溶解，钝化不锈钢纤维表面并提高不锈钢纤维分散性；铜包集束不锈钢纤维细拉丝在电解剥离过程中，作为其酸性电解液添加剂使用，添加量可按原酸解液的体积为参数，30-60ml/L添加；可能产生稳流或稳压电解的电流及电压在适当范围内变化； 不锈钢纤维酸解处理液添加量小，提高其剥离速度1-4倍，良好的纤维分散性及表面色泽，其纤维表面抗氧化能力显著增强。 The stainless steel fiber is treated by acid electrolysis, and the stainless steel fiber is cleaned and dried with pure water after electrolysis; as the additive of acid electrolytic solution, it can improve the acid electrolytic separation speed of stainless steel fiber after bundle drawing, promote the rapid dissolution of copper, passivate the surface of stainless steel fiber and improve the dispersion of stainless steel fiber; the copper bundle is not rusty In the process of electrolytic stripping, the steel fiber fine drawing can be used as the additive of acid electrolyte. The addition amount can be 30-60ml / L according to the volume of the original acid hydrolysate. The current and voltage of the steady current or steady voltage electrolysis may change in an appropriate range; The results show that the addition of acid hydrolysis solution of stainless steel fiber can increase the peeling speed by 1-4 times, and the fiber surface has good dispersion and surface color, and its surface oxidation resistance is significantly enhanced. |
| 上一页 钢纤维混凝土影响因素 |
| 下一页 碳钢弹簧钢丝常用铅浴淬火工艺 |
Copyright © 技术支持：遨游网络