| 钢纤维的主要性能 |
| 添加时间：2018/9/3 17:45:14 浏览次数： |
| 钢纤维是一种新、高性能的钢纤维品种。钢纤维道路的配合比设计方法大体与普通混凝土相同，不同点为：强度双控标准（抗压强度和弯拉强度）；钢纤维掺量根据设计要求的弯拉强度确定；单位用水量和砂率与纤维掺量有关，每掺加0.5%（体积率）钢纤维，单位用水量增加6kg，砂率增大2%。 Steel fiber is a new and high performance steel fiber variety. The mix ratio design method of steel fiber road is basically the same as that of ordinary concrete, the difference is: strength double-control standard (compressive strength and flexural tensile strength); steel fiber content is determined according to the flexural tensile strength of design requirements; unit water consumption and sand rate are related to fiber content, every 0.5% (volume ratio) steel fiber is added, unit water consumption. When the volume increased by 6kg, the sand rate increased by 2%. 钢纤维混凝土具有与普通混凝土一样的搅拌、运转和施工性能，纤维在混凝土中不会结球，分布均匀，可在商品混凝土搅拌站进行生产并能用于泵送施工。铣削钢纤维混凝土的早期坍落度损失较大，30分钟损失32%，2小时损失42%。钢纤维混凝土的实际工作性优于相同的坍落度的普通混凝土。钢纤维混凝土具有良好的材料性能，与普通混凝土相比，其抗压强度提高2～20%；弯拉强度提高20～50%；劈裂抗拉强度提高20～40%；耐磨性能提高40%左右，其物理力理性能完全可以满足城市道路工程及检查井盖等配套构件需求技术指标。钢纤维粗糙而洁净的表面，能与混凝土中的水泥浆体牢固的结合，这是铣削钢纤维提高混凝土各种性能的根本原因。[1] Steel fiber reinforced concrete (SFRC) has the same mixing, operation and construction performance as ordinary concrete. Fibers do not form pellets in concrete and distribute evenly. It can be produced in commercial concrete mixing station and used in pumping construction. The early slump loss of milling steel fiber reinforced concrete is larger, the loss of 30 minutes is 32%, and the loss of 2 hours is 42%. The actual workability of steel fiber reinforced concrete is better than that of ordinary concrete with slump. Steel fiber reinforced concrete (SFRC) has good material properties. Compared with ordinary concrete, its compressive strength is increased by 2-20%; its flexural tensile strength is increased by 20-50%; its splitting tensile strength is increased by 20-40%; its wear resistance is improved by 40%. Its physical and mechanical properties can completely meet the needs of supporting components such as urban road engineering and inspection well cover. Indicators. The rough and clean surface of steel fiber can combine firmly with cement paste in concrete, which is the fundamental reason why milling steel fiber can improve the performance of concrete. [1] 此外，高强钢钎维混凝土在铁道轨枕预制、高速公路伸缩缝、水泥砼道面等预制、现浇、生产施工等方面均已得到大量应用，其优良性能完全可以取得良好的技术经济和社会环境效益。 In addition, high-strength steel brazed concrete has been widely used in the prefabrication of railway sleepers, expansion joints of expressways, cement concrete pavement, cast-in-situ, production and construction, etc. Its excellent performance can achieve good technical, economic and social environmental benefits. |
| 上一页 不锈钢纤维 |
| 下一页 钢纤维被分成四大类 |
Copyright © 技术支持：遨游网络