新闻动态
夏季保存钢纤维有什么技巧
由于夏季雨水较多、气候环境潮湿的原因,钢纤维极易发生氧化生锈的情况,钢纤维的表面附着一层镀锌层,该镀锌层如果过厚(当然越厚越不易生锈)会达不到SGS环保标准;但是如果钢纤维镀锌层过薄,就容易和水分子发生氧化作用,造成生锈。潮湿环境对钢纤维的保存有一定的影响。
Because of rainwater and humid climate in summer, steel fibers are prone to oxidative rusting. A galvanized layer is attached to the surface of steel fibers. If the galvanized layer is too thick (of course, xuzhisu.07858.net shilayou.07858.net fangtingyou.07858.netdaoreyou.07858.nethaerbin.89ix.comhuhehaote.89ix.comthe thicker the rust), it will not meet the SGS environmental protection standard. But if the galvanized layer of steel fibers is too thin, it will be easy to oxidize with water molecules and cause rust. The wet environment has a certain effect on the preservation of steel fibers.
关于钢纤维的储存环境,在雨季需注意车间、仓库的空气湿度,建议用测湿器测纸张值8-10之间,通常书纸比粉纸的吸湿度要大些,且pH值也较高更需注意出现钢纤维生锈现象。 一般来讲在正常环境下存贮钢纤维(除了氧化室),存放两年的时间是不会发生钢纤维被腐蚀的现象的,但要注意在搬运钢纤维过程中须轻拿轻放避免钢纤维外包装受到磨损。总结来说,对于钢纤维的存放环境,建议可以适当把湿度控制为50%以下,温度控制在10℃-30℃之间就可以了。
As for the storage environment of steel fibers, attention should be paid to the air humidity of workshop and warehouse in rainy season. It is suggested that the paper value should be measured between 8 and 10 by humidity detector. Usually, the moisture absorption of book and paper is higher than that of shijiazhuang.89ix.comhefei.89ix.com nanning.89ix.comwuhan.89ix.comtangshan.89ix.comzhangjiakou.89ix.compowder paper, and the higher pH value, the more attention should be paid to the phenomenon of steel fibers rusting. Generally speaking, steel fibers stored in normal environment (except oxidation chamber) will not be corroded for two years, but it should be noted that in the process of handling steel fibers, it is not necessary to handle lightly to avoid wear and tear of steel fibers packaging. In summary, for the storage environment of steel fibers, it is suggested that the humidity should be controlled below 50% and the temperature should be controlled between 10 and 30 degrees centigrade.
Because of rainwater and humid climate in summer, steel fibers are prone to oxidative rusting. A galvanized layer is attached to the surface of steel fibers. If the galvanized layer is too thick (of course, xuzhisu.07858.net shilayou.07858.net fangtingyou.07858.netdaoreyou.07858.nethaerbin.89ix.comhuhehaote.89ix.comthe thicker the rust), it will not meet the SGS environmental protection standard. But if the galvanized layer of steel fibers is too thin, it will be easy to oxidize with water molecules and cause rust. The wet environment has a certain effect on the preservation of steel fibers.
关于钢纤维的储存环境,在雨季需注意车间、仓库的空气湿度,建议用测湿器测纸张值8-10之间,通常书纸比粉纸的吸湿度要大些,且pH值也较高更需注意出现钢纤维生锈现象。 一般来讲在正常环境下存贮钢纤维(除了氧化室),存放两年的时间是不会发生钢纤维被腐蚀的现象的,但要注意在搬运钢纤维过程中须轻拿轻放避免钢纤维外包装受到磨损。总结来说,对于钢纤维的存放环境,建议可以适当把湿度控制为50%以下,温度控制在10℃-30℃之间就可以了。
As for the storage environment of steel fibers, attention should be paid to the air humidity of workshop and warehouse in rainy season. It is suggested that the paper value should be measured between 8 and 10 by humidity detector. Usually, the moisture absorption of book and paper is higher than that of shijiazhuang.89ix.comhefei.89ix.com nanning.89ix.comwuhan.89ix.comtangshan.89ix.comzhangjiakou.89ix.compowder paper, and the higher pH value, the more attention should be paid to the phenomenon of steel fibers rusting. Generally speaking, steel fibers stored in normal environment (except oxidation chamber) will not be corroded for two years, but it should be noted that in the process of handling steel fibers, it is not necessary to handle lightly to avoid wear and tear of steel fibers packaging. In summary, for the storage environment of steel fibers, it is suggested that the humidity should be controlled below 50% and the temperature should be controlled between 10 and 30 degrees centigrade.