超钢纤维与其他钢纤维经济型比较
超钢纤维是针对钢纤维的进途进行研制的，它的截面形状及比表面积和钢纤维相似，因此在比较两种材料的经济性时，可假设它们比表面积相同，超钢纤维的比重为0.95kg/cm-3，钢的比重为7.8kg/cm3，同样体积掺量下，钢纤维重量是超钢纤维重量的8.0倍。因此，不难看出用超钢纤维代替钢纤维可较大幅度降低成本。
Super steel fibers are developed for the future of steel fibers. Their cross-sectional shape and specific surface area are similar to those of steel fibers. Therefore, when comparing the economy of the two www.quyangdiaoke.net.cnwww.renwushidiao.com.cnwww.shibeidiaoke.cnwww.rewudiaosu.cnmaterials, it can be assumed that they have the same specific surface area. The proportion of super steel fibers is www.oushibilu.cnwww.quyangshidiao.net.cn0.95 kg/cm-3 and that of steel is 7.8 kg/cm-3. Under the same volume content, the weight of steel fibers is 8.0 times that of super steel fibers. Therefore, it is not difficult to see that using super steel fibers instead of steel fibers can greatly reduce costs.
Super steel fibers are developed for the future of steel fibers. Their cross-sectional shape and specific surface area are similar to those of steel fibers. Therefore, when comparing the economy of the two www.quyangdiaoke.net.cnwww.renwushidiao.com.cnwww.shibeidiaoke.cnwww.rewudiaosu.cnmaterials, it can be assumed that they have the same specific surface area. The proportion of super steel fibers is www.oushibilu.cnwww.quyangshidiao.net.cn0.95 kg/cm-3 and that of steel is 7.8 kg/cm-3. Under the same volume content, the weight of steel fibers is 8.0 times that of super steel fibers. Therefore, it is not difficult to see that using super steel fibers instead of steel fibers can greatly reduce costs.